All Activity. This will help minimize the possibility of theft. High Heat: 1850/1900F, hold 30/45 minutes at temperature. The resultant microstructure is ferrite and carbide. Do not heat faster than 400 degrees per hour. #8. Can anyone give me the procedure for heat treating 440c stainless and for tempering also. Usually the time to hold at temp. I wrap the knives in stainless steel foil so they'll have less exposure to the oxygen inside the kiln, place them in the kiln, and bring the temperature to 1400 F. The knives soak at this temperature for 15 minutes to ensure the blades are preheated all the way through. However, VG10 looks closer to 440C than it does 19C27. So, I don't really need to know the specs on forging it, but I do need to know how to heat treat the steel. Heat at a rate not exceeding 400F per hour (222C per hour) to 1000-1050F The 440c is a high carbon stainless steel alloy under the 440 series. There are those who want you to believe the only way to achieve a good heat treat is by using a temperature regulated heat treating oven, soaking for 15.7 minutes, normalized 2.3 times, and then quenched in park's knife heat treating oil raised to exactly 134.6 degrees Fahrenheit. I would never use stainless mystery steel. Thanks, Ted One of the hardest types of stainless steel after heat treating, 440C offers excellent wear and abrasion resistance. This is the most important part, and the most time-sensitive. . Quench: Air, positive pressure vacuum, interrupted oil. Tempering: Temper at 400F for one hour, two times However, without additional finishing, 440c may only achieve moderate corrosion resistance, which can be detrimental over the life of a component. I hope this helps others who are trying to heat treat their stainless knifes. Raise heat to 1950 F and hold for one hour. Aluminium Quench Plates. Put just your name and address. Post Falls, ID 83854-5200. PETERS HEAT TREAT Cutlery Treatment Peters' Heat Treating provides services for the custom knife maker. On your address label to us, do not put "custom knives". Heat slowly to 1400 - 1450 for O-1 and 1375 - 1425 for O-2. AUS-10 has higher toughness than 440C. 440C is one of the best stainless steels for knifemaking, within its limitations. A 6.35-mm-thick and 50.8-mm-wide hot-rolled 440C bar purchased from Admiral Steel was used for this work. West Yorkshire Steel are suppliers of 440C stainless steel in round bar, diameters. 1 x Quart Liquid Degreaser. It also requires shielding from oxygen such as foil wrap to protect the steel. A stainless knife steel is not going to have the wear resistance of a tool steel like D2, or the hardness of a high carbon steel like 1095, or the elasticity of a spring steel like 5160. Share. #2 Send them out. 440C (UNS designation S44004) is a martensitic 400 series stainless steel, and is the highest carbon content from 400 stainless steel series. I heat treat high alloyed stainless steels, including but not limited to Crucible CPM S35-VN, CPM S30V, CPM 154, Timken-Latrobe BG 42, Hitachi ATS 34, Uddeholm Elmax Superclean, Sandvik 13C26, AEBL, 440C,Damasteel, and Nichols stainless damascus. By Will W., May 4, 2017 in Heat Treating Knives, Blades etc. 440C Hardening : **Knives should be cleaned by washing with soapy water and then either placed into a foil pouch or coated with high temperature anti-scale/decarburization compound prior to heat treat if not using Oxygen free heat treat equipment. 440C stainless steel falls under the high carbon martensitic stainless steel category. Crucible Steel has online data sheets for heat treating their steels and they do make 440C. Ship package to: Paul Bos Heat Treating. 440C Stainless Steel Alloy Composition: Recommended Heat Treatment Seal blade in double crimped high temperature? I use an Evenheat electric oven. Heat treatment methods, such as stress relieving, hardening and annealing, strengthen the ductility and corrosion resistance properties of the metal that is modified during fabrication, or generate hard structures capable of tolerating abrasion and high mechanical stresses. for hardening is given for 1" of thickness but their are other variables as well. BladesIIB 3.09K subscribers Looking for the recipe or step by step ramp hold instructions for heat treating and tempering 440C Stainless Steel and CPM154 Stainless Steel Knife blades,. Grade 440C is capable of attaining, after heat treatment, the highest strength, hardness and wear resistance of all the stainless alloys. Likes (Received) 53. The process is the same for any simple high carbon steel. Applications Typical applications include: Its very high carbon content of 1.0% is responsible for these characteristics, which make 440C particularly suited to such This grade should be allowed to cool slowly after forging. Never heat color knife blades or previously heat colored or tempered parts. Since 440C is a stainless steel, I created a new heat treat schedule where I pre-heat the blades at 1400F and hold for 10 minutes followed by ramping to 1900F and holding for 30 minutes. Furnace cool at rate of 20 per hour to 900 F, than air cool. Following poor heat treatment, 440C steel's corrosion resistance will fall behind, along with edge retention and sharpness. 1. 440C stainless steel contains C 1.2% carbon, this steel has good rust resistance, is currently imported in mass production of . But it is not for the weak of heart or newcomer to the game. ***Skipping stages such as pre-heating and equalizing or cryo will result in lower hardness, higher last week, I received my first commission to make a set of 9 steak knives. After cooling most also need sub zero or cryogenic, ie. However, the edge retention can be greatly increased if AEB-L steel is hardened to well in such a way that the hardness level goes beyond . Temps are close to 2000f for most stainless steels. Heat treating 440C. All alloy steel soften during the heating process and the same goes for 440a steel. dry ice and acetone mix, or liquid nitrogen to deal with retained austentite. Oil hardening steels up to 24" and all others up to 50" in length. The as-received hardness was 17.6 R C, corresponding to 96.5 R B. I've hardened 3/16 440C in a 150 degree canola oil bath and it worked without any distortion I couldn't correct. The steel has moderate corrosion resistance and is thus perfect for knife blades and other mid-range cutting tools. Heat treatment of austenitic stainless steel Cr, Ni and other alloying elements in austenitic stainless steel result in the Ms point down to below room temperature (-30 to -70 ). Check hardness and austenitize no higher than the peak hardness. Side note: The fact that I am using a RR spike knifeto demonstrate the HT doesn't change the process in any way, it's just the knifeI had on hand that needed finished up. 440C Stainless Preheat thoroughly at 1400/1500F and hold for 30 minutes. The steel must be heat treated to get to a hardened state. Among the many different high carbon stainless steels used for knives, 440C is very comparable to AUS-10. The more chromium the more carbide is formed. 440C grade provides good wear resistance combined with moderate corrosion resistance in mild environments and has excellent hardenability. Includes material certificates and CAD models. CPM 154, Timken-Latrobe BG 42, Hitachi ATS 34, Uddeholm Elmax Superclean . Check Prof. Larrin Thomas's article on heat treatment of AEB-L stainless steel. So, I ordered 3 lengths of 1/8 X 1" X 36" 440C from Admiral Steel and have already decided this is going to be a stock removal project. Crucible 440C is a heat treatable stainless steel, designed for a combination of high wear resistance and moderate corrosion resistance in mild environments. 2 x Cans For Degreasing and Quenching. Austenitise at 1040?C for 30 minutes. It's best to work in a darkened room to better observe the color. The chemical composition of 440C steel is a mixture of high Chromium (17%) and high Carbon (more than 1%), which makes stainless steel with great wear resistance and corrosion resistance. Reheating should be used if necessary. Heat treatment of 440c steel typically proceeds as follows: 1. 440C should be forged at 1950 to 2050F and finished not lower than 1750F. J. 0,02% of Sulfur: Increases machinability. Stainless steels are heat-treated based on the stainless steel type and the target end item requirements. 440C stainless steel is a high carbon type of stainless, this is the alloy most often used for knife-making. This can also be done wit. The excellent wear and resistant qualities of 440-C steel make it the natural choice of knifemakers. Average Brinell Hardness - 202. . 440c Steel hardness (Rockwell Hardness) 440c Steel has a hardness of 57HRC. Instructions with color chart. Hence, it exhibits high strength. The corrosion resistance varies from good to moderate. I purchased an Evenheat 27" LB kiln a little over a year ago. The oil quench method has made a lot of good stainless knives over the years, and although cryo has proven benefits, I certainly don't focus on it. Heat treating 440C - Heat Treating Knives, Blades etc - I Forge Iron. To ensure the stability of the austenitic organization, so that when heating and cooling, the phase change does not occur above room temperature. It's often used for bearings, valves, and knife blades. Hold at temperature for at least 1.5 hours per inch of greatest thickness. Sep 28, 2011. Other steel makers may have data also. Overheating steel into the 1550F to 1600F range and beyond and soaking it will grow grain. If you want to go stainless: Get 440c in 1/8 or 3/16ths and grind to shape. Full annealing Full annealing is done at a temperature range between 850 - 900 C, after which it is slowly cooled in the furnace to about 600 C and then air-cooled to room temperature. The Kit Includes: 1 x 2lb Tub Casweld Keep Kool Putty. If you want to learn knife making get some basic knife making carbon steel and a good book. 3. And please list your source. It is usually heat treated to reach hardness of 58-60 HRC.It is a bearing steel, and used in rolling contact stainless bearings, e.g. Subzero freeze at 200 below 0. Answer: Standard vacuum processes used in the bearing industry for 440C typically yields hardness values in the 58-62 HRC range. 440-C Stainless Steel Mill Finish from $22.10 440-C is a high-carbon chromium stainless that resists corrosion from fresh water, steam, crude oil, gasoline, stains from food acids and fruit. 440C stainless steel has greater abrasion and wear resistance for use in bearing and bushing applications. Also check with the bp on heat treating in the files. Tempering: Temper at 400F for one hour, two times ____________________________________________ ATS-34 Stainless 440C Stainless steel is a heat treatable stainless steel that has been designed for very good wear resistance with moderate corrosion resistance in mild environments. 440C and AUS-10 perform the same in many areas, except for toughness. Up to now I only used it for heat treating carbon steel knives. Heat Treatment of 440a Stainless Steel. The linear coefficient of thermal expansion for 440C steel is approximately 11 x 10^-6 /C or about 6 x 10^-6 /F. I like to temper for the full 2 hrs, twice, regardless of thickness. It is worth noting that AEB-L stainless steel is still lower than that of 440C stainless steel. The composition of the bar was measured via optical emission spectroscopy (OES) and is shown in Table I along with the target composition based on information from the supplier. 123. A few minutes at this temperature will not grow grain but does allow the carbon to get "into solution". This process removes any prior heat treatment and makes the metal soft enough to grind or otherwise shape. Allow the blade to cool slowly inside the furnace to room temp. Heat the steel to be hardened to orange hot. So a piece of 440C steel that is raised to the austenitizing temperature and then cooled, will expand (a little) as it is heated and then shrink back to original size once it is cooled. 440C Stainless Steel Bar. Subzero freeze at 200 below 0. Stainless needs precise temp control such as a kiln will provide. Air quench at room temperature. Order fulfillment usually takes about 5-8 working days of shop time after receiving blades. They are easy to work and heat treat is doable at home with a forge. Without any further ado, let's get started. It has the same ~1% carbon as 19C27 and 440C, but intermediate chromium content of 15%, whereas 19C27 has 13% and 440C has 17%. 660 S. Lochsa Street. To check your heat treatment against mine, it is best to perform heat treatments from a range of austenitizing temperatures and going straight into the cold treatment used, whether freezer, dry ice, or liquid nitrogen. Heat the blade in the furnace 800-850C (1470-1560F) and hold for 30 minutes. The reason for softening is in the tempering of steel. The method we use to heat treat 440C SS knife blades. Fuel your obsession by reading . Instructions For Steel & Stainless Steel Parts. AEB-L steel Toughness. Plate quench with? Its very high carbon content is responsible for these characteristics, which make 440C particularly suited to such applications as ball bearings and valve parts. Step 1 Place the blank, the unfinished piece that will become your knife blade, in the heat treating oven and heat slowly to between 1,550 and 1,650 degrees Fahrenheit to anneal it. 440C can be oil quenched to achieve maximum . LSS440C Stainless Knife Steel HEAT TREATING INSTRUCTIONS (See Tech-Topics Bulletin 102 for a more thorough explanation of heat treating.) It contains the highest carbon content in its series, which gives the steel its characteristic hardness, wear-resistance, and strength. Dip the blade of a knife or edge or a work tool to he hardened into motor oil and allow to cool. 1 x Quart Quenching Oil. Preheat to 760?C, hold for 5 minutes. Annealing 440C should be annealed for maximum softness by thorough soaking at 1650F for six hours followed by a furnace cool. We heat treat ALL grades of steel. 440C is very similar to the 440B grade but with a slightly higher carbon content. That is the color of a ripe orange. Choose from over 550 440C stainless steel products in a wide range of sizes. This involves preheating at 1440F (780C) for 45-60 minutes and then ramping to 1940F (1060C), soak for 45-60 minutes and gas (nitrogen) quench - basically backfilling with nitrogen to -5 inches Hg and fan cooling. 440C Stainless Heat treatment sheet for reference Preheat thoroughly at 1400/1500F and hold for 30 minutes. Parts Must Be Polished or sanded first. Hot rolled and annealed. You should foil wrap or use anti-scale compound that can handle that heat range (ATP-641 from brownells works for me). Overview: 440C Stainless steel is a type of modern steel and famous for its high corrosion resistant, wear resistance, strength and hardness qualities, among all the stainless alloys, capable of attaining (after heat treatment) the highest hardness (60 HRC). How to Heat Treat a knifein the simplest and easiest way possible. Air quench at room temperature. 440C Stainless Steel, ESR .202 in 23.5 in 1.5 in $35.40 - + Add to Cart 440C Stainless Steel Information and Composition Condition: This alloy been properly annealed and is in the soft condition. discover knife making tips of the pros, learn proper grinding of knife blades and proper heat treatment. After heat treatment, 440c steel has the highest strength, hardness, and wear resistance of all stainless alloys due to its high carbon content. But none of them is going to have the corrosion resistance of 440C. ATP-641 Anti Scale Compound. 2. Your hobby has become your obsession. There is ample evidence in the literature that the austenitization temperature and a post-quench liquid nitrogen soak play a significant role in the hardness/strength of martensitic . 309 Heat Treating Foil / Tool Wrap ?or coat in? When the metal is tempered the same expansion . Heat treating requires a temp controlled oven that can hold at 1900f. Clean the metal with a wire brush to remove any scale and wash in dawn dishwashing liquid to remove oil. AISI 440C steel is the best steel in the 440 series, it has the highest carbon content with 440A (0.7% C), 440B (.85% C), and 440C (1.05% C); the Rockwell hardness goes up with carbon but the corrosion resistance, in turn, goes down.. 440C Carbon steel is a genuine type of stainless steel because it contains more than enough amounts of chromium (18%) in its composition. Corrosion resistant only in the hardened condition. If you're using quench plates then this step is generally not needed. The steel has good hardness as well as good wear resistance. But in most cases, 440C stainless steel's corrosion resistance is better than other stainless steel. It has good resistance to the atmosphere, fresh water and mild acids. . All blades are evaluated upon arrival for damage during shipment, straightness, special fixturing needs and heat treating requirements. Simple, heat it to non-magnetic, give it another minute or so to heat a bit more, quench. Nice steels include 1084, 1095 and 5160. . HARDENING: Preheating: To minimize distortion in complex tools use a double preheat. The common heat treatment applied on 440a steels include annealing and hardening tempering and welding is also accompanied by post and pre weld heat treatments. Preheat: 1100/1250F, equalize, 1400/1450F, equalize. 440C Revised May 2008 Page 1 of 2 www.atlassteels.com.au Grade 440C is capable of attaining, after heat treatment, the highest strength, hardness (Rockwell C 60) and wear resistance of all the stainless alloys. Raise heat to 1950 F and hold for one hour. Martensitic stainless steel has the same characteristics of hardening by quenching as alloy steel, so a wide range of different mechanical properties can be obtained by selecting the grade and heat treatment conditions. Can be heat treated for high strength and hardness. You do not have to do any non-standard wasteful processes before heat treating. Typical chemistry . All three of those steels are contain primarily chromium carbide. ball bearings and roller bearings.It is also used to make knife blades. The results are used to rationalize and select an optimum heat-treat process for a knife fabricated in anticipation of the 2017 TMS Bladesmithing competition.